DIN 30NiCrMo16-6
Osaka
Designation by Standards
| Brand Name | Ravne No. | Mat. No. | DIN | EN | AISI |
| PO954 | 954 | - | 30NiCrMo16-6 | - | - |
Chemical Composition (in weight %)
| C | Si | Mn | Cr | Mo | Ni | V | W | Others |
| 0.30 | 0.25 | 0.50 | 1.40 | 0.45 | 4.00 | - | - | - |
Applications
For quenching and tempering.
Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 210
Density [g/cm3]: 7.85
Forging
Hot forming temperature: 1050-850oC.
Forms manufactured
Please see the Dimensional Sales Program.
Disclaimer
The information and data presented herein are typical or average values and are not a guarantee of maximum or minimum values. Applications specifically suggested for material described herein are made solely for the purpose of illustration to enable the reader to make his own evaluation and are not intended as warranties, either express or implied, of fitness for these or other purposes. There is no representation that the recipient of this literature will receive updated editions as it become available.
Designation by Standards
| Brand Name | Ravne No. | Mat. No. | DIN | EN | AISI |
| PO954 | 954 | - | 30NiCrMo16-6 | - | - |
Chemical Composition (in weight %)
| C | Si | Mn | Cr | Mo | Ni | V | W | Others |
| 0.30 | 0.25 | 0.50 | 1.40 | 0.45 | 4.00 | - | - | - |
Applications
For quenching and tempering.
Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 210
Density [g/cm3]: 7.85
Forging
Hot forming temperature: 1050-850oC.
Forms manufactured
Please see the Dimensional Sales Program.
Disclaimer
The information and data presented herein are typical or average values and are not a guarantee of maximum or minimum values. Applications specifically suggested for material described herein are made solely for the purpose of illustration to enable the reader to make his own evaluation and are not intended as warranties, either express or implied, of fitness for these or other purposes. There is no representation that the recipient of this literature will receive updated editions as it become available.