Mat.No. 1.2747/DIN X210Cr12/AISI D3
Designation by Standards
| Mat. No. | DIN | EN | AISI |
| 1.2747 | X210Cr12 | - | D3 |
Chemical Composition (in weight %)
| C | Si | Mn | Cr | Mo | Ni | V | W | Others |
| 2.05 | 0.25 | 0.30 | 11.50 | - | - | - | - | - |
Applications
Pilger mandrels up to diameter 140-200mm.
Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 210
Density [g/cm3]: 7.85
Soft Annealing
Heat to 620-680oC, cool slowly.
Stress Relieving
Stress relieving to remove machining stresses should be carried out by heating to 600-650oC, holding for one hour at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
Hardening
Harden from a temperature of 840-870oC followed by oil or air quenching.
Tempering
Tempering temperature: 620-670oC.
Forging
Hot forming temperature: 1050-850oC.
Forms manufactured
Please see the Dimensional Sales Program.
Disclaimer
The information and data presented herein are typical or average values and are not a guarantee of maximum or minimum values. Applications specifically suggested for material described herein are made solely for the purpose of illustration to enable the reader to make his own evaluation and are not intended as warranties, either express or implied, of fitness for these or other purposes. There is no representation that the recipient of this literature will receive updated editions as the become available.
Designation by Standards
| Mat. No. | DIN | EN | AISI |
| 1.2747 | X210Cr12 | - | D3 |
Chemical Composition (in weight %)
| C | Si | Mn | Cr | Mo | Ni | V | W | Others |
| 2.05 | 0.25 | 0.30 | 11.50 | - | - | - | - | - |
Applications
Pilger mandrels up to diameter 140-200mm.
Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 210
Density [g/cm3]: 7.85
Soft Annealing
Heat to 620-680oC, cool slowly.
Stress Relieving
Stress relieving to remove machining stresses should be carried out by heating to 600-650oC, holding for one hour at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
Hardening
Harden from a temperature of 840-870oC followed by oil or air quenching.
Tempering
Tempering temperature: 620-670oC.
Forging
Hot forming temperature: 1050-850oC.
Forms manufactured
Please see the Dimensional Sales Program.
Disclaimer
The information and data presented herein are typical or average values and are not a guarantee of maximum or minimum values. Applications specifically suggested for material described herein are made solely for the purpose of illustration to enable the reader to make his own evaluation and are not intended as warranties, either express or implied, of fitness for these or other purposes. There is no representation that the recipient of this literature will receive updated editions as the become available.